Thin Film Coating Packaging for Device Having Meltable and Wetting Links

ABSTRACT

A method for creating a dielectric thin-film coating for devices having a fusible element is disclosed. The method comprises mixing insoluble and soluble polymers in solid form and exposing the mixture to heat to create a melt mixture. The melt mixture is then dissolved in a solvent to create a slurry which can then be deposited on the device as a thin-film coating to create an interior insulation layer or an external surface.

FIELD OF THE INVENTION

the present invention relates generally to the field of circuit protection devices and, in particular, to fuses, thermally-protected metal-oxide varistors (TMOVs) and thermal cut-off devices (TCOs).

BACKGROUND OF THE INVENTION

Fuses and TMOVs are commonly-known circuit protection devices typically installed between a source of electrical power and a component in the electrical circuit that is to be protected. Devices such as fuses and TMOVs have meltable links that will melt in an overcurrent or overvoltage condition. Such devices may be low-profile or wafer-based devices and may be covered with a dielectric coating that accommodates de-wetting. However, the current packaging for such devices is difficult to deposit due to its relative thickness. As such, current dielectric coatings are expensive and difficult to deposit on a scale below 50 μm.

Ideally a coating for a meltable link would meet three criteria. First, the coating should have dielectric properties. In particular, the coating should act as an insulator. Second, the coating should be able to cover the meltable link while not restricting the meltable link from flowing once the link has reached its melting temperature. Some current coatings may hold the meltable link in place after the link has reached its melting temperature, thereby restricting the circuit from opening. Third, the covering should be able to be deposited when in the solution phase to create coatings on the scale of 50 μm or less.

Current methods of coating these devices fail to meet all three criteria. For instance, some polymers, silicon polyester and polypropylene, when used as a coating will meet the first criteria of having dielectric properties but fail to meet the second criteria of covering the meltable link without restricting the flow of the link after melting. Current devices may use a polymer from the polyamide family, which may meet the first two criteria but fail to meet the third criteria of being able to be deposited from a solution phase, thereby resulting in a thin coating layer.

Therefore, would be desirable to have a coating for low-profile and wafer-based devices having meltable links that meet all three of the criteria.

SUMMARY OF THE INVENTION

A coating for devices having meltable links may be created by a method which includes the steps of melt mixing an insoluble polymer with a soluble polymer and exposing the melt mixed to a solvent that will create a slurry which may then be deposited with any well-known technique, for example, by spin coating, deep coating, drip coating, etc. Coatings created in accordance with the present invention may be used as an insulation layer on the interior devices or may be used as an exterior coating.

Devices made on a wafer and/or extremely small devices are thus able to have a thin dielectric coating that eliminates expensive packaging. The coating can accommodate controlled de-wetting that will allow the fast opening of the devices for and will also serve to protect any exposed metal surfaces of the device from corrosion.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a photographic depiction of the prior art example of a device having a meltable link.

FIG. 2 is a flowchart showing the steps of the method for producing and applying the coating of the present invention.

FIG. 3 is a schematic diagram of a device having a meltable link, showing the covering of the present invention in place on the device.

DETAILED DESCRIPTION

The solution-based coating of the present invention creates a thin dielectric layer suitable for use over a meltable link. The coating serves as packaging and creates a low profile for a fuse or TMOV. The dielectric film accommodates wetting properties of the fuses and generate packaging film on the scale of 50 microns

FIG. 1 is a photographic representation of a portion of a device having a meltable element. The devices to metal electrodes 102, typically made from copper which are bridged by a solder ball 104. Solder ball 104 is designed to melt in reaching a certain temperature and open the circuit. The device of FIG. 1 is typical of the type of devices which would benefit from the coating of the present invention.

FIG. 2 is a flowchart showing the steps of a method 200 for creating the coating of the present invention. In step 202, the insoluble polymer and the soluble polymer are combined. The insoluble and soluble polymers are commercially available and come in the physical form of pellets or chips.

In some embodiments, the insoluble polymer may be selected from a group comprising polyamides and their copolymers and grafted materials (e.g., hot glue). In other embodiments, low temperature high density polyethylene (HDPE) or low density polyethylene (LDPE), low Tg (glass transition temperature) PETs, soluble or semi-soluble EBA, EMA polymer family (referred by the general term of hot glues and fatty acids or wood pitches, often referred as rosin, may be used as the insoluble polymer. In a preferred embodiment, the insoluble polymer is a polyamide. The insoluble polymer typically is in the form of pellets ranging in size from ⅛″ to ¼″ in size.

Many soluble polymers are possible for use in this invention. In some embodiments, the soluble polymer may be for example, soluble polyurethanes or waxes, which are soluble in DMF or aromatic solvents, such as xylene, toluene or anisole, or any other soluble polymer. In other embodiments of the invention, the soluble polymer may be a polyamic acid or PVDF, which are soluble in DMF or NMP. In general, any soluble polymer may be used as long as the soluble polymer has a melting point below about 130° C., or below the melting point of the solder link, does not constrain the molten solder and does not, better suppress arcing. In a preferred embodiment of the invention, a low melting temperature polyurethane is used as the soluble polymer. Soluble polymers typically are in the form of chips ranging in size from ½ mm to 5 mm.

The insoluble and soluble polymers may be mixed in an insoluble to soluble ratio of about 75:25, but in preferred embodiments, the ratio would be between 40:60 and 60:40.

In step 204, the insoluble and soluble polymer pellets are melted to create a melt mixture by exposing to heat. The mixture may be melted and mixed by an industrial machine containing a heating element and mixing blades, or, preferably, an extruding machine capable of heating and mixing the insoluble and soluble polymer to create the melt mixture and thereafter extruding the melt mixture into a wire or fiber having a relatively small cross-section.

The temperature at which the insoluble and soluble polymers are melted is dependent upon the selection of specific polymers, but, in general, the mixture may be heated to at least the temperature of the material having the higher melting point. In other embodiments, the mixture may be melted at a temperature between the melting points of the insoluble and soluble polymers, wherein the mixing blades of the mixing machine create a sheer force within the mixture that tends to increase the temperature of the mixture. In some embodiments of the invention, the melt mixture may be cut into small pallet size pieces as it exits from the extruding machine to increase the surface area of the melt mixture.

Step 206 of the process is an optional step in which the melt mixture is allowed to cool and solidify and, in optional step 208, the solidified melt mixture is cut into chip or pallet size pieces to increase the surface area. In other embodiments of the invention, steps to a 206 and 208 may be skipped and the melt mixture may be extruded or otherwise placed in melted form directly into a solvent.

In step 210 of the process, the melt mix is exposed to a solvent, and when mixed, will eventually create a slurry. The increased surface area of the melt mixture created by cutting the melt mixture into pallet size pieces makes the process of creating the slur easier. The solvent may comprise, for example, xylene, toluene, anisole, DMF (Dimethylformamide) or NMP (N-Methylpyrrolidone), or any solvent capable of dissolving the soluble polymer. The choice of solvent is highly dependent on the choice of soluble polymer. The melt mixture and solvent are mixed in a ratio of approximately 3 parts weight melt mixture and 7 parts weight solvent but again, this is highly dependent on the choice of polymers and solvents. The resulting slurry may have a viscosity of between 1 cps and about 10,000 cps.

In step 212, once the slurry is been created it may be informally deposited on the device as either an interior insulating layer or an exterior coating. The coating may be applied by any well-known means, for example, spin coating, deep coating, drip coating, etc.

FIG. 3 shows a typical device having copper electrodes 304 joined by a meltable link 302, typically, solder ball. The conformal coating of the present invention is shown as 306 in the figure.

The coating made in accordance with the method disclosed herein meets all three design criteria set forth in the Background of the Invention. The method creates a dielectric coating having insulating properties. The coating, once conformally deposited on a meltable element, allows the meltable element to flow when the meltable element reaches but its melting point. Lastly, the coating can be applied as a thin-film in the range of 50 μm in thickness and, as such, is suitable for use with low-profile TMOVs and other wafer-based devices. 

We claim:
 1. A method for creating thin-film coating, comprising: mixing and insoluble polymer and soluble polymer in solid form; creating a melt mixture of the insoluble polymer in the soluble polymer by heating and mixing the insoluble polymer and the soluble polymer; exposing the melt mixture to a solvent to create a slurry; and depositing the slurry on a device to create a coating.
 2. The method of claim 1, wherein the insoluble polymer is selected from a group comprising polyamides, copolymers, low temperature high density polyethylene, low density polyethylene, PETs, soluble or semi-soluble EBA, and EMA polymers.
 3. The method of claim 1 wherein the insoluble polymer is a polyamide.
 4. The method of claim 1, wherein the soluble polymer selected from a group comprising soluble polyurethanes or waxes, polyamic acid and PVDF.
 5. The method of claim 1 wherein the soluble polymer is a low melting temperature polyurethane.
 6. The method of claim 1, wherein the solvent is selected from a group comprising xylene, toluene, anisole, DMF and NMP.
 7. The method of claim 1, wherein the insoluble polymer and soluble polymer are present in the melt mixture in a ratio of between 40:60 and 60:40.
 8. The method of claim 1, wherein the melt mixture and solvent are mixed in a ratio of 3 weight parts melt mixture and 7 weight parts solvent.
 9. The method of claim 1, wherein the insoluble polymer the soluble polymer are heated to a melting temperature of the component having the highest melting temperature.
 10. The method of claim 1, wherein the slurry is deposited on the device using a method selected from a group comprising spin coating, deep coating and drip coating.
 11. The method of claim 1, wherein the device is a device comprising a meltable element between two electrodes and further wherein the thon-film coating covers at least the meltable element.
 12. The method of claim 1 wherein the thin-film coating has dielectric properties.
 13. The method of claim 1, wherein the thin-film coating allows the meltable element to flow away from the electrodes after the meltable element has reached its melting point.
 14. The method of claim 1, wherein the thin-film coating is less than 50 microns in thickness.
 15. A device comprising: one or more electrodes; a meltable link electrically joining the one or more electrodes; and a thin-film coating covering the pone or more electrodes and the meltable link; wherein the thin-film coating is formed by depositing a slurry comprising a melt mixture of insoluble and soluble polymer and a solvent onto the device.
 16. The device of claim 15, wherein the slurry is deposited on the device using a method selected from a group comprising spin coating, deep coating and drip coating.
 17. The device of claim 15, wherein the thin-film coating allows the meltable element to flow away from the electrodes after the meltable element has reached its melting point.
 18. The device of claim 15, wherein the insoluble polymer is selected from a group comprising polyamides, copolymers, low temperature high density polyethylene, low density polyethylene, PETs, soluble or semi-soluble EBA, and EMA polymers.
 19. The device of claim 15, wherein the soluble polymer selected from a group comprising soluble polyurethanes or waxes, polyamic acid and PVDF.
 20. The device of claim 15, wherein the solvent is selected from a group comprising xylene, toluene, anisole, DMF and NMP. 